Elemento de prueba | Método de ensayo | Unidad | T3170 | T3175 | T3180 | T3185. | T3190 | T3195 | T3390 |
La gravedad específica | La norma ASTM D792 | G/cm3 | 1.18 | 1.18 | 1.19 | 1.19 | 1.20 | 1.21 | 1.22 |
La dureza | La norma ASTM D2240 | Shore A | 72 | 75 | 81 | 92 | 96 | 96 | |
Fuerza tensil | La norma ASTM D412 | MPa | 21 | 23 | 27 | 30 | 38 | 41 | 38 |
Elongación final | La norma ASTM D412 | % | 870 | 890 | 750 | 640 | 550 | 540 | 530 |
100% modular | La norma ASTM D412 | MPa | 3 | 4 | 44 | 5 | 8 | 12 | 11 |
300% modular | La norma ASTM D412 | MPa | 4 | 5 | 7 | 8 | 17 | 19 | 17 |
La fuerza de corte | La norma ASTM D624 | KN/m | 65 | 76 | 89 | 106 | 132 | 137 | 138 |
Temperatura de procesamiento | / | °C. | 165-190 | 170-195 | 180-200 | 185-205 | 190-215 | 200-220 | 200-210 |